Background Bone tissue engineering, based on three-dimensional (3D) printing technology, has emerged as a promising approach to treat bone defects using scaffolds. The objective of this study was to investigate the influence of porosity and internal structure on the mechanical properties of scaffolds. Methods We fabricated composite scaffolds (which aimed to replicate trabecular bone) from polycaprolactone (PCL) reinforced with 30% (wt.) nano-hydroxyapatite (nHAp) by extrusion printing. Scaffolds with various porosities were designed and fabricated with and without an interlayer offset, termed as staggered and lattice structure, respectively. Mechanical compressive testing was performed to determine scaffold elastic modulus and yield strength.…

Scaffolds play a key role in bone tissue engineering (BTE) as they provide a mechanically and biologically supportive template to treat bone defects. Yet, the ideal scaffold structures are far from certain, leaving a lot to be discovered in terms of the scaffold structure–performance relationships. In this study, we investigated the influence of pore size and internal structure on osteoblast performance in vitro. Three-dimensional (3D) scaffolds were printed from polycaprolactone (PCL) reinforced with 30% (wt.) nano-hydroxyapatite (nHAp), with two different internal structures (lattice and staggered) and four pore sizes (0.280, 0.380, 0.420, and 0.550 mm). Scaffolds were seeded with pre-osteoblast…